To explore the annealing temperature dependence of dielectric properties $Ta_2$$O_{5}$ thin films were prepared by MOCVD(metal-organic chemical vapor deposition) and MOD(metal-organic decomposition). The $Ta_2$$O_{5}$thin films fabricated MOCVD and MOD were annealed in $O_2$at temperature between 600 and 90$0^{circ}C$. The measured dielectric constant of both films at 100 KHz was the highest value at $650^{circ}C$ and decreased with increasing annealing temperature above $650^{circ}C$. Plane-view SEM image showed that the boundary seems to be crack broke out with increasing annealing temperature. It was confirmed that outbreak of boundary influenced a decrease of dielectric constant with increasing annealing temperature. The leakage current density increased with increasing annealing temperature.