The oxidation behaviors of Y-Cr bilayer deposited on ferritic steel by magnetron-sputtering for application of the Fe-Cr alloys as interconnectors of planar-type solid oxide fuel cells (SOFCs) were studied. After oxidation at $800^{circ}C$ for 40 hours, the major phase of $Y_2$$O_3$and the minor phase of $YCrO_3$, $Mn_{1.5}$ $Cr_{1.5}$ $O_4$and Cr$_2$SiO$_4$were formed in the Y/Cr bilayered samples, while the major phase of Cr$_2$O$_3$and the minor phase of $Y_2$$O_3$were formed as the major phase in the Cr/Y bilayered samples. The Log(ASR/T) that expresses electric resistance of the Y/Cr coated specimen with nonconducting $_Y2$$O_3$oxide showed high value of -2.80 Ω$ extrm{cm}^2$$K^{-1}$ / and that of the Cr/Y coated specimen with conducting $Cr_2$$O_3$oxide appeared to be -4.11 Ω$ extrm{cm}^2$$^{K}$ . The electric resistance of the Y/Cr coated specimen was largely increased due to the formation of high resistance oxide scales. However, the Cr/Y coated specimen did not show any increase in the electric resistance and had the long-term stability of oxidation because there was no formation of the secondary phases with low conductivity.