In order to prepare the uniform copper particles from copper sulfate solution by using hydrazine as a reduction agents, the reduction behavior of copper particles from copper sulfate was investigated in detail at room temperature by the observation of reaction products. The effects of $NH_4$OH and $Na_4$$P_2$$O_{7}$ on the formation of uniform copper particles were discussed. ($NHCu_3$)$_4$$SO_4$was completely formed at over pH 11 by adding $NH_4$OH in copper sulfate solution. The fine $Cu_2$O with the particle size of 50 nm was produced in the initial reduction process of (NH$Cu_3$)$_4$$SO_4$solution with $Na_4$$P_2$$O_{ 7}$ and then the Cu$_2$O was converted into copper particles by inserting additional hydrazine. When Cu(NH$_3$)$_4$SO$_4$solution with $Na_4$$P_2$$O_{ 7}$ was reduced at $80^{circ}C$ by hydrazine, the highly dispersed copper particles with the particle size of about 0.8 $mu extrm{m}$ was obtained.