The electromagnetic properties and microstructures of the ferrites based on ($Ni_{0.2}$ $Cu_{0.2}$ $Zn_{0.6}$)$_{1.085}$($Fe_2$$O_3$)$_{0.915}$ were investigated by changing the amount of additive SnO$_2$and CaO and the sintering temperatures. Addition of $SnO_2$caused pores in the specimen. There was no variation of grain size by changing the amount of additives. Total loss was reduced when ($Ni_{0.2} $Cu_{0.2}$ $Zn_{ 0.6}$)$_{1.085}$ ($Fe_2$$O_3$)$_{0.915}$ composition was sintered at $1150^{circ}C$ rather than $1300^{circ}C$. Addition of CaO was useful to reduce the total loss because it increased the sintering density. The lowest total loss was obtained when 0.06 wt% $SnO_2$and 0.4 wt% CaO were added at the same time.