TiNi bodies were produced from (Ti＋Ni) powder mixture by spark-plasma sintering procerg. The sintering behavior was investigated through the measurement of change in density, densification rate, phase analysis and microstructure. Irrespective of heating rate, sintered bodies with above 97％ relative density could be obtained. TiNi with B2 structure was confirmed as the major phase and $Ti_2Ni,;TiNi_3$, unreacted Ti, Ni as the second phase. Increase in heating rate suppressed a formation of intermediate phase during sintering process. Increase in holding time at sintering temperature led to a compositional homogenization.