The influences of mixed strain mode of bending-tension on the critical current. Ic in externally reinforced Bi-2223 tapes and their interaction were investigated in this study. A test fixture which providing a mixed deformation mode of bending-tension to HTS tapes has been newly devised. When the total strain induced in the tape in the mixed strain mode was expressed by the superposition of the bending and tensile strains the irreversible strain for the critical current degradation of Bi-2223 tapes increased, as compared with the simple bending mode case. The $I_c$ degradation at the region exceeding the irreversible strain showed a medium between the simple bending case and the simple tension case. As the initial bending strain imparted increased , namely as the diameter of mandrel adopted decreased. the apparent irreversible strain in Bi-2223 tapes increased . but the increment became smaller As a result. it can be found that the tension to be applied to bent Bi-2223 tapes during cabling should be smaller. as the mandrel diameter becomes smaller.