TiO$_2$, SiO$_2$, and PBA(Pseudo Boehemite Alumina) sol were prepared by sol-gel process. The particle sizes of these sol exhibited uniform 10∼30 nm. As the amount of SiO$_2$ sol increased, the temperature of phase transition (from anatase phase to rutile phase) was raised temperature than $600^{circ}C$, which attributed to the enhanced photocatalyst properties. Also, the anatase phase was obtained with very small amount of the rutile phase from the addition of SiO$_2$ (10∼30 wt%) at annealing temperature of 120$0^{circ}C$. The specimen with 20 wt% SiO$_2$ sol exhibited the maximum photocatalyst properties. But, the specimen with PBA sol did not affect photocatalytic activity due to the presence of rutile phase.