AZO (Al-doped ZnO) thin films were deposited on glass by pulsed magnetron sputtering method, and their structural, electrical and optical properties were investigated. XRD patterns showed that a highly c-axis preferred AZO film was grown in perpendicular to the substrate when pulse frequency of 30 ㎑ was applied to the target. Microstructure of thin films showed that the fibrous grain of tight dome shape was grown. The deposition rate decreased linearly with increase of pulse frequency, and the lowest resistivity was 8.67${ imes}$10$^$-4/ $Omega$-cm for the film prepared at pulse frequency of 30 ㎑. The optical transmittance spectra of the films showed a very high transmittance of 85∼90%, within visible wavelength region and exhibited the absorption edge of about 350 nm. The characteristics of the low electrical resistivity and high optical transmittance of AXO films suggested a possibility for the application to transparent conducting oxides.