In this study, 0.96B $i_{0.5}$($Na_{0.84}$ $K_{0.16}$)$_{0.5}$Ti $O_3$ + 0.04SrTi $O_3$ + 0.3 wt% N $b_2$ $O_{5}$+0.2 wt% L $a_2$ $O_3$ + xwt % Mn $O_2$ were investigated as a function of the amount of Mn $O_2$ addition in order to improve dielectric and piezoelectric properties of Lead-free piezoelectric ceramics. With increasing the amount of Mn $O_2$ addition, the density, electromechanical coupling factor( $k_{p}$), piezoelectric constant( $d_{33}$, $g_{33}$) and curie temperature (Tc) showed the maximum value of 5.7 g/㎤, 38 %, 219 pC/N, 26 mVㆍm/N and 32$0^{circ}C$ at 0.1 wt% Mn $O_2$ addition, respectively, and mechanical quality factor( $Q_{m}$ ) showed the maximum value of 158 at 0.3 wt% Mn $O_2$ addition.ddition.ion.n.