Two-dimensionally arrayed nanocolumn lattices were fabricated by using double-exposure laser holographic method. The hexagonal lattice was formed by rotating the sample with 60 degree while the square lattice by 90 degree before the second laser-exposure. The reactive ion etching for a typical time of 30 min using CH$_4$/H$_2$ plasma enhanced the aspect-ratio by more than 1.5 with a slight increase of the bottom width of columns. The etch-damage was observed by photoluminescence (PL) spectroscopy which was removed by the wet chemical etching using HBr/$H_2O$$_2$/$H_2O$ solution, leading into the enhanced PL intensities of the PCs.