After extrusion, cold rolling and T-6 treatment, texture development of 7x1x Al-alloy with 0.1% Sc is studied. During extrusion the very strong <111>+weak <100> fiber texture is developed, which is Influenced on the formation of rolling texture. The texture after 80% cold rolling can be described by strong{112}<111>(Cu)+{123}<634>(S) component in the cross section of the extruded rod, the strong -fiber+weak{110}<001>(Goss) components in the longitudinal section, and the strong {110}<112>(Bs)+weak{001}<100>(Cube) components in the transverse section. The components of rolling texture are remained after T-6 treatment, but the maximum density of ODF is higher. The calculated mean r-values and the planar anisotropy are relatively high, which are dependent on the texture. After T-6 treatment, recrystallized equiaxed grains with average grain size of $1{sim}2{mu}m$ are obtained