This study is to investigate a damage estimation of single edge notched tensile specimens as a function of acoustic emission(AE) according to the uni-directionally oriented carbon fiber/epoxy composites, CFRP In fiber reinforced composite materials, AE signals due to several types of failure mechanisms are typically observed. These are due to fiber breakage, fiber pull-out matrix cracking, delamination, and splitting or fiber bundle breaking. And these are usually discriminated on the basis of amplitude distribution, event counts, and energy related parameters. In this case, AE signals were analyzed and classified 3 regions by AE event counts, energy and amplitude for corresponding applied load. Bath-tub curve shows 3 distinct periods during the lifetime of a single-edge-notch(SEN) specimen. The characterization of AE generated from CFRP during SEN tensile test is becoming an useful tool f3r the prediction of damage failure or/and failure mode analysis.