Synthesis of the non-swelling property micas was carried out by hydrothermal method. In order to artificially induce the diffusion of ions, a rotating system was attached to the hydrothermal apparatus and by adding 0.7 mm zircon beads, synthesis of the non-swelling property micas could be performed in a low temperature area. The hydrothermal conditions for the preparation of micas were a reaction temperature of $260^{circ}C$, for 72 hrs, using $1K_2O,;1Al(OH)_3,;4Mg(OH)_2;and;6SiO_2$ as the starting materials and a 8M-KOH solution as the hydrothermal solvent. The micas obtained under these conditions were a plate shape with a size of $2.89{mu}m$ and showed a whiteness of over 97 %. Also, through the FT-IR analysis, because the absorption peak of the $Mg_3OH$ vibration was observed at approximately $3700cm^{-1}$, it could be known that it was phlogopite of non-swelling property showing the chemical composition of $KMg_3AlSi_3O_{10}(OH)_2$. This result was very consistent with the EDS analysis where O (41.34 %), Mg (3.88 %), Al (11.45 %), Si (17.62 %) and K (25.71%) elements were detected.