The $MgB_2$ tapes with several metal powder addition were fabricated by PIT method with or without heat treatment. The $J_c$ value of $5.600A/cm^2$ and $16.000A/cm^2$ at 4.2 K and 5 T were obtained for the $MgB_2$ tape and 10 vol % of Cu added $MgB_2$ tape without heat treatment respectively. The $J_c$ value of $8.000A/cm^2$ and $35,000A/cm^2$ at 4.2 K and 5 T were obtained for the $MgB_2$ tape and 10 vol. % of Al added $MgB_2$ tape with heat treatment, respectively. The $J_c-B$ curve shows enhancement in $J_c$ under magnetic field. which suggests enhancement in workability and grain connectivity with several metal powder addition.