The W/O emulsion was formed by mixing hydrophobic nonion surfactants of span 80 and tween 60 with kerosine, and by adding sodium silicate aqueous solution. Precipitating the W/O emulsion by sodium bicarbonate resulted in spherical silica particles. Shape and size distribution of silica particles were observed. The particles were spherical and they have narrow size distribution. Particle sizes were 9.29, 7.39 and $5.73;{mu}m$ at homogenizer speed of 2500, 3000, and 3500 rpm, respectively. The particle size was decreased by increasing agitation speed due to the formation of emulsion droplet. At fixed agitation speed, absorbed paraffin oil weight were measured and the $SiO_2/Na_2O$ mole ratio effects on particle size were investigated. Particle size was decreased by increasing the mole ratio of $SiO_2/Na_2O$.