The SCT thin films are deposited on Pt-coated electrode($Pt/TiN/SiO_2/Si$) using RF sputtering method with Sr/Ca ratio. The maximum grain of thin films is obtained by ratio of Ca at 15 mol%. The dielectric constant was increased with increasing the ratio of Ca, while it was decreased if the ratio of Ca exceeded over 15 mol%. The dielectric constant changes almost linearly in temperature ranges of $-80{sim}+90$. All SCT thin films used in this study show the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 200 kHz. The current-voltage characteristics of SCT thin films showed the increasing leakage current as the measuring temperature increases.