In practical applications of HTS tapes for electric devices such as coils and power cables, the jointing of HTS tapes is inevitable even though long length tapes have recently been achieved. The critical current, $I_c$, degradation behaviors with tensile and bending deformations were investigated in commercially available YBCO coated conductor tapes. When the V-I relationship was measured at the jointed section of the lap-jointed YBCO CC tapes, the resistance at the joint decreased with increasing joint length. The critical load for 95% $I_c$ retention were determined for the IBAD and RABiTS YBCO tapes and they were 175 and 355N, respectively. Fracture occurred at the unjointed part which represents strong copper lamination and solder jointing. The electro-mechanical properties of lap-jointed CC tapes depended on the properties of single tapes. The V-I behavior under bending strain was similar with the tensile case.