We report the results of MOD-processed YBCO coated conductors on the IBAD-MgO template. The precursor solution was coated on the $CeO_2-buffered$ IBAD-MgO template using a slot-die coating method, calcined at a temperature of $550^{circ}C$, and fired at high temperatures for 2.5 h in a reduced oxygen atmosphere. The $J_C$ value of YBCO coated conductors was found to be very sensitive to the microstructure, and thus higher $J_C$ value could be achieved when the in-plane texture was higher and the difference in $T_{C,zero}$. was negligible. Optimally processed YBCO coated conductor exhibited $J_C$ value of $0.75MA/cm^2$ at 77 K in self-field, which might be due to somewhat depressed $T_{C,zero}$ of 87.3 K caused by possible $Sm^{3+}$ substitution on the $Ba^{2+}$ site.