The influence of water partial pressure in Metal-organic Deposition (MOD) method was investigated on the texture and the morphology of $YBa_2Cu_3O_{7-x}$ (YBCO) films grown on the buffered metal tapes. The water partial pressure was varied from 4.2% up to 10.0% with the other process variables, such as annealing temperature and oxygen partial pressure, kept constant. In this work, the fluorine-free Y & Cu precursor solution added with Sm was synthesized and coated by the continuous slot-die coating & calcination step. The next annealing step of the YBCO films was done by the reel-to-reel method with the gas flowed vertically down. From the x-ray diffraction analysis, the un-reacted phase like $BaF_2$ peak was found at the water partial pressure of 4.2%, but $BaF_2$ peak intensity is much reduced as the water partial pressure is increased. However, the higher water partial pressure of about 10% in this experiment leads to the poor crystallinity of YBCO films. The morphologies of the YBCO films were not different from each other when the water partial pressure was varied in this work. The maximum critical current density of 3.8MA/$cm^2$ was obtained at the water partial pressure of 6.2% with the annealing temperature of 780$^{circ}C$ and oxygen partial pressure of 500ppm.