In this study, brazing characteristics of the dissimilar Ti and Cu metals using a Zr-base amorphous filler ($Zr_{41.2}Ti_{13.8}Cu_{12.5}Ni_{10.0}Be_{22.5}$ in at.%) have been investigated for various bonding temperatures. In the sample brazed at $790^{circ}C$ for 10 min., the Ti-rich phases in the joint were observed, while the Cu-rich phases were obtained in the sample brazed at $825^{circ}C$ for 10 min.. Such a different microstructure and composition in the joints could be explained by the degree of the dissolution reaction. At $790^{circ}C$, the reaction between the Zr-rich liquid phase and the Ti base metal was actively occurred to form Ti-rich liquid phase in the joint. As the temperature increased to $825^{circ}C$, however, the reaction between the Ti-rich liquid phase and the Cu base metal was promoted to form the Cu-rich liquid phase in the joint finally. Such a different interface reaction is attributed to the reactivity or solubility between the Zr as a main element in the filler and the Ti and Cu as a base metal element.