Effects of ferrite grain size on static and dynamic deformation behaviors of SCM415 stels were investigated in this study. Dynamic torsional test was conducted using torsional Kolsky bar with the strain rate of $1.6{ imes}10^3/s$. Specimens with three different grain size of ferrite, $4.6{mu}m$, $11{mu}m$, $35.5{mu}m$ were used. Dimple fracture mode of the dynamic test specimens showed adiabatic shear bands on the beneath of fracture surface. Increased uniform elongation and decreased non-uniform elongation appeared as grain size of ferrite decreased in dynamic torsional test. However, shear strength was independent on grain size of ferrite.