In this study, the effects of initial texture on the twinning formation of AZ31 Mg rolled sheet was investigated. Uniaxial compression tests were carried out on samples cut along the normal direction(ND) and roiling direction(RD), respectively, of rolled AZ31 Mg alloy sheet at various temperatures (RT, 200, 250, 300, 350, $400^{circ}C$) with the fixed strain rate($10^{-2}/s$). The results showed that deformation twining occurred actively only in the RD specimens, which promoted homogeneous deformation as compared to the ND specimens. The effect of temperature on the formation of deformation twins was also investigated, and the slip/twin transition temperature was found to be approximately $250^{circ}C$.