Lanthanum aluminate($LaAlO_3$) film has been prepared on single crystal and metal substrates by dip coating method. Lanthanum acetate and aluminum were prepared via ligand exchange starting from lanthanum nitrate hexahydrate and aluminum nitrate hexahydrate in acetate glacial acetic acid solution after being refluxed. Coating solution was obtained by diluting the gel with methanol and 2-methoxyethanol to adjust the total cation concentration to 0.67 M. Precursor coated film was prepared by dip-coating with a speed of 25 mm/min on various substrates such as $LaAlO_3$ (001), MgO(001), $SrTiO_3$(001) single crystal, LMO/MgO/Ni-alloy. Thin films have been obtained by heat treating the precursor film at various temperatures from $600^{circ}C{sim}900^{circ}C$ and various heating rate from $0.83^{circ}C/min{sim}1.25^{circ}C/min$ under $Ar/O_2$ mixture containing 1000ppm oxygen. The films have been characterized by scanning electronic microscopy (SEM) and X-ray diffraction (XRD). XRD analysis for the prepared film showed that $LaAlO_3$ thin films with a preferred orientation of (100) plane parallel to substrate surface were obtained at $800^{circ}C(1.11;^{circ}C/min)$ on LMO/MgO/Ni-alloy substrate, but the intensity decreased with the increase of heat treatment temperature.