[ $YBa_2Cu_3O_{7-{delta}}$ ] films have been prepared on $LaAlO_3$ (100) single-crystal substrates by the metal organic deposition using dichloroacetate precursors (DCA-MOD). DCA precursor solutions with different composition such as; Yttrium-excess(15 at%), barium-poor(25 at%), and a stoichiometric(Y:Ba:Cu=1:2:3) were prepared in order to investigate the effects of precursor composition on the properties of YBCO films prepared by DCA-MOD method. Coated films were calcined at low temperature up to $500^{circ}C$ in flowing humid oxygen atmosphere. Conversion heat treatment was performed $800^{circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. For the film prepared using excess yttrium composition, high critical current density ($J_c$) of $>2MA/cm^2$ was obtained whereas, for the films prepared using barium-poor composition, $J_c$ was lower than $1MA/cm^2$.