In this paper, the influences of poling electric field on piezoelectric properties of $0.95(K_{0.5}Na_{0.5})NbO_3$-$0.05Li(Sb_{0.8}Nb_{0.2})O_3$ (abbreviated as KNN-LSN) ceramics were investigated. The specimens was sintered at sintering temperature of $1050^{circ}C$. They showed orthorhombic phase structure without secondary phase. Electromechanical coupling factor (kp), dielectric and piezoelectric constant($d_{33}$) increased with poling electric field. However, mechanical quality factor (Qm) decreased. Take into account of poling conditions and piezoelectric properties of KNN-LSN ceramics, the optimum poling condition for KNN-LSN ceramics was poling electric field of 4.5 kV/mm. At the time, kp of 0.458, Qm of 43.97, $d_{33}$ of 278 pC/N, and dielectric constant of 1079 were shown, respectively.