SiOC thin film of hybrid-type that is the limelight as low dielectric material of next generation were deposited by plasma enhanced chemical vapor deposition (PECVD) method with bistrimethylsilylmethane (BTMSM) precursor increased by 2 sccms from 24 sccms to 32 sccm. Manufactured samples are analyzed components by measuring FT/IR absorption lines. It is a tendency that seems to be growing of Si-O-Si(C) bonding group and narrowing of Si-O-$CH_3$ bonding group relative to the increasing flow-rate BTMSM. The chemical shift in the XPS analysis was shown in the specimens between the BTMSM=26 sccm and BTMSM = 28 sccm. The binding energy of Si 2p, C 1s and O 1s electron orbit spectra was the low-est at the specimen of the BTMSM=26 sccm. From the results of electrical Properties using the 1 MHz C - V measurements, the dielectric constant was 2.32 at the specimen with the BTMSM = 26 sccm.