In this study, in order to develop excellent lead-free composition ceramics for piezoelectric transformer, ($K_4CuNb_8O_{23}$) added $(K_{0.5}Na_{0.5})(Nb_{0.96}Sb_{0.04})O_3$ ceramics were fabricated using conventional mixed oxide method and their piezoelectric and dielectric properties were investigated as a fu+EY50nction of the amount of KCN addition. With increasing the amount of KCN addition, density and mechanical quality factor(Qm), electromechanical coupling factor (Kp) were increased up to 1.2 mol% and then decreased. At the 1.2 mol% KCN added specimen, mechanical quality factor (Qm), electromechanical coupling factor (Kp), density and dielectric constant (${varepsilon}r$) showed the optimal values of 781, 0.445, $4.42;g/cm^3$ and 443, respectively, for piezoelectric transformer application.