In this research, the composites (100-x)LCP-xBNT (x = 0, 10, 20, 30, 40 vol.%) were fabricated with thermoplastic LCP(Liquid Crystal Polymer) and BNT($BaNd_2Ti_4O_{12}$) which is a high frequency dielectric material. Their dielectric properties, mechanical strength and microstructure were investigated by Impedance analyser, Instron and SEM. In order to fabricate LCP-BNT composites, LCP resin was put into the twin screw type mixer($310^{circ}C$), melted by keeping for 10 min. After that, BNT filler was dispersed with melted LCP resin for 15 min. in the mixer. For measuring the dielectric properties and mechanical strength, Composite specimens were made by pressing composite granule (LCP-BNT) with 7 ton in the mold at $310^{circ}C$. With increasing the BNT content (0~40 vol.%) of the composite, Its dielectric constant increased, dielectric loss and flexural strength decreased. The dielectric constant and flexural strength of composites with 20~30 vol.% of BNT filler are 4.1~6.0 and 35~55 MPa respectively. BNT/LCP composite is the potential substrate material for the high frequency application.