We report the studies on the structrural properties of Langmuir Blodgett (LB) films fabricated from the copolymer of vinylidenefluoride (VDF) with trifluoroethylene(TrFE). The formation of nanomesas induced by thermal annealing at $135;^{circ}C$ for 1 hour was investigated with the atomic force microscope (AFM) and the X-ray diffractometer (XRD). From the result of surface morphology change in 30 monolayer LB film, we find that the annealing treatment on the P(VDF-TrFE) LB film result in the plastic deformation of crystalline polymer. The ${eta}$ phase crytalline structure in annealed LB film was clearly confirmed from the XRD peak at $19.7^{circ}$.