Dynamic rheological properties of PP-based long glass fiber-reinforced thermoplastics (LFT) were investigated. Weight fractions of the glass fibers investigated in the present study ranged from 0.15 to 0.5, which are higher than those of previous studies. We observed very abnormal rheological behavior. Complex viscosity (${eta}^*$) of the LFT increased with the glass fiber content up to 40 wt. %. However, the ${eta}^*$ with a weight fraction of 0.5 is observed to be lower than that of LFT with a weight fraction of 0.4 in spite of higher glass fiber content. From various experiments, we found that this abnormal behavior is analogous to the rheological behavior of a lyotropic liquid crystalline polymer solution and concluded that the abnormal rheological behavior for the LFT is attributed to the formation of a liquid crystal- like structure at high concentrations of long glass fibers.