In order to improve the adhesion between poly-monochloro-para-xylylene (Parylene-C) film and Aluminum thin film, the surface of Parylene-C film was irradiated by ${O_2}^+$ and $Ar^+$ ion beam generated by duoplamatron ion source. The ion dose of $Ar^+$ and ${O_2}^+$ was changed from $5{ imes}10^{14}$ to $1{ imes}10^{17}/cm^2$ and the ion beam energy was 1 kV. Contact angles of water on Parylene-C modified by $Ar^+$ and ${O_2}^+$ ion irradiation decreased from $78^{circ}$ to around $17^{circ}$, and $9^{circ}$, respectively. X-ray photoelectron spectroscopy analysis shows that the hydrophilic groups were formed on the surface of Parylene-C by chemical reaction between the unstable chains induced by the ion irradiation and oxygen ions or residual oxygen gas. The hydrophilic groups were identified as C-O bond, C=O bond and (C=O)-O bond. The cross cut tape test which was applied to characterize the adhesion between Al thin film and Parylene-C film modified by ${O_2}^+$ ions irradiation shows that the adhesion strength was improved as increasing ion dose.