We have studied structural, optical, and electrical properties of the Al-doped ZnO (AZO) thin films using RF magnetron sputtering with various working pressure. To find optimal properties of AZO for transparent conducting oxides, the working pressure in sputtering process was varied as 0.07 Torr, 0.02 Torr, and 0.007 Torr, respectively. As working pressure increased, the crystallinity of AZO thin film was improved, the surface roughness of AZO thin film decreased. The transmittance of the film was over 80% in the visible light range regardless of the changes in working pressure. In case of 0.007 Torr, best electrical properties was shown due to the reduction of oxygen absorption by decreasing surface roughness.