Phenyltrimethoxysilane (PTMS) was anchored onto the sensitized $TiO_2$ nanoparticles. This insulating molecular layer effectively inhibited the charge recombination at the interface of $TiO_2$/electrolyte in the dye-sensitized solar cells (DSCs) without sacrificing the dye-loading capacity of the nanocrystalline $TiO_2$. DSCs using PTMS-modified $TiO_2$ exhibited a short-circuit current ($J_{SC}$) of $15.9mA/cm^2$, an open-circuit voltage ($V_{OC}$) of 789 mV, and a fill factor (FF) of 68.2%, yielding an overall conversion efficiency (${eta}$) of 8.55% under $100mW/cm^2$ illumination. The resulting cell efficiency was improved by ~10% as compared with the reference cell.