We fabricated $(Li_{0.5-x}Na_xLa_{0.5})Ti_{0.8}Zr_{0.2}O_3$(LNTLZ)ceramics ($0{leq}x{leq}0.4$) with a perovskite structure via standard solid state synthesis. The influence of Na content on the structural and electrical properties of LNTLZ ceramics was also investigated. During XRD patterns analysis, all of the samples showed orthorhombic structure. The resistance of LNTLZ ceramics decreased as Na content increased, and the maximum activation energy shows 0.56 eV at x=0.4 at room temperature. These results indicated that LNTLZ ceramics are a candidate for use Lithium ion batteries as electrolytes.