In this study, surface characteristics and corrosion behaviors have been investigated in addition to Zr elements on the low elastic modulus Ti-30Ta alloy. Low elastic modulus Ti-30Ta-xZr(x : 3, 7 and 15 wt %) alloys were prepared by arc melting and then heat treated at $1000^{circ}C$ for 24 hrs in an argon atmosphere. Microstructures of the alloys were examined by field emission scanning electron microscope(FE-SEM) and X-ray diffractometer(XRD). Electrochemical experiments were performed using a conventional three-electrode configuration with a sample working electrode, a high density carbon counter electrode and a saturated calomel reference electrode. According to the result of polarization behavior in the Ti-30Ta-xZr alloys, the current density of homogenized Ti-30Ta-15Zr in the passive region was lower than the other alloys.