Influences of Co and inhibitors from nano-sized WC materials were observed in the sintering process. VC and $Cr_3C_2$ were used as inhibitors. The crystal structure and surface images of sintered nano-sized WC materials, as functions of Co and inhibitors, were evaluated by XRD and FE-SEM analyses. The relative densities of sintered nano-sized WC materials did not change even with increased quantity of Co and increased temperature. The density of sintered nano-sized WC materials with inhibitors was lower than that of sintered nano-sized WC materials without inhibitors. No difference in hardness due to change of inhibitors was found.