In this present study, the luminescence characteristics and mechanism of energy $CaTiO_3$:Pr phosphor were studied using disk specimens sintered at various temperatures and envirenment. A single-phase $CaTiO_3$:Pr was synthesized by sintering above 140$0^{circ}C$ and its crystal structure was found to be perovskite orthorhombic. A dominant peak around 360 nm and a broad peak around 395 nm were observed in the PLE(Photoluminescence Excitation) spectrum of $CaTiO_3$:Pr with fixed emission wavelength at 612 nm, the decay time of 360 nm excitation was found to be longer than that of 395 nm excitation. From this result, it is assumed that the free carrier excited to 360 nm is transferred to 395 nm energy level. Therefore, the decrease in 395 nm intensity observed in CaTiO$_3$:Pr specimens sintered in Ar gas environment induced shorter decay time and improved CL luminescence.