We evaluated the electric properties of Bi-2223 jointed tapes processed by both resistive-and superconducting-joint methods. For resistive-joint. filler materials of wood metal Pb/Sn. In and silver paste were used whereas for superconductive-joint lap joint method was used. In the resistive joint tape. critical transport property(CCR) n-value and contact resistance were observed to be in the range of 10-85% 1-8,9. and 0.71x10$^$-6/-0.13x10$^$-6/Ω, respectively. depending on their filler materials. Specifically it is believed that the electrical properties of resistive joint tape are significantly related to the resistivity of filler materials. On the other hand the CCR of superconductin joint type was varied 55 to 85% with uniaxial pressure probably due to the irregular microstructure in the transition region.